	Reinforced or graphite-coated aramid and mineral fibres						Synthetic fibres
	LATTYcarb96		LATTYcarb965		LATTYcarb96 G2F		LATTYgold5 Acid
Operating Conditions standard associated non-associated	-196/290°C 45bar 450°C 130bar		-196/290°C 50bar 450°C 150bar		-196/290°C 50bar 450°C 130bar		-196/150°C 16bar 200°C 60bar
Applications	Polyvalent. HP steam. All hydrocarbons.		Polyvalent. HP steam. All hydrocarbons.		Polyvalent. HP steam. All hydrocarbons.		Highly aggressive media like mineral acids and bases.
Composition	Carbon and mineral fibres.		Carbon and mineral fibres with metal reinforcement.		Carbon and mineral fibres with special two-sided graphite coating for easier removal.		Synthetic fibres and resins.
Technical Characteristics
Density NFT 48-102	1.7		1.9		1.7		1.85
Tensile strength NFT 48-103 • Perpendicular direction of fibres	10 N/mm²		1.4 N/mm²		10 N/mm²		10 N/mm²
Ignition loss NFT 48-104 DIN 52911	24%		-		24%		26%
Relaxation at 300°C DIN 52913	35N/mm²		35 N/mm²		35 N/mm²		30 N/mm² (at 200°C
Compressibility ASTM 36 A	10-14%		10-14%		10-14%		10%
Elastic recovery ASTM 36A	>55%		>60%		>55%		>45%
Elastic limit • 20°C •200°C	150 N/mm² >50 N/mm²		>150 N/mm² >50 N/mm²		>150 N/mm² >50 N/mm²		>150 N/mm² >50 N/mm²
Gas tightness DIN 3535/6	<1cm³/min		<2cm³/min		<1cm³/min		<1cm³/min
Behaviour after immersion in: •NFT 48-001 - 48-105 •DIN 3754-1 - BS 1832	m%	e%	m%	e%	m%	e%	m%	e%
• B type solvent (at 23°C - 48h)	<12	<8	12	<8	<12	<8	H2SO465% (at 23°C - 48h) <5	<10
• ASTM oil No.3 (at 150°C - 5h)	<14	<5	<14	<5	<14	<5	HNO350% (at 23°C - 48h) <5	<8
• ASTM oil No.1 (at 100°C - 70h)	-	-	<7	<3	-	-	NaOH40% (at 23°C - 48h) <5	<5
• Distilled water (at 100°C - 48h)	<8	<4	<8	<4	<8	<4	-	-
Observations or treatments	-		Graphite-coated		Graphite-coated		-
Standards	BS 7531 grade-X		BS 7531 grade-X		BS 7531 grade-X		-

Standard Sizes	1 x 1.50m and 2 x 3m (2 x 5m on request)
Standard thicknesses	1-1.5 - 2 and 3mm (0.5 - 0.8 and 4mm: consult us)